The synthetic Gosu currently used throughout Japan was developed by the Fukaumi family during the early Meiji period (late 19th century)

釉薬の品質を最大限引き出していただきたいため、釉薬ご利用時のよくある問題点とその対策を下記になります。ぜひご一読ください。

磁器の場合：天草撰中

3319チタン茶マットNo.2 (1.8L) new As a general rule[Firing conditions for sample plates] Clay components <br>For porcelain: Amakusa Senchu (SiO2 72. 04% Al2O3 18. 16% Fe2O3 0. 65% TiO2 0. 04% CaO 0. 49% MgO 0. 09% Na2O 0. 58% K2O 3. 00% Ig. Loss 4. 55%) For pottery: Umezaki red clay (SiO2 72. 11%, Al2O3 15. 98%, Fe2O3 2. 12%, TiO2 0. 67%, CaO 0. 12%, MgO 0. 36%, Na2O 0. 58%, K2O 2. 47%, Ig. Loss 5. 16%) Firing temperature : Reduction: 1280 Glazing : Baume concentration 50 (soak for about 3 seconds)